The radical copolymerization of methyl methacrylate and 2-hydroxyethyl methacrylate was carried out via atomtransfer radical polymerization (ATRP) initiated by ethyl 2-bromoisobutyrate and catalyzed by CuBr/2,2'-bipyridinecomplex. This polymerization proceeds in a living fashion with controlled molecular weight and low polydispersity. Theobtained copolymer was esterified with 2-bromoisobutylryl bromide yielding a macroinitiator, poly(methyl methacrylate-co-2-hydroxyethyl methacrylate-co-2-(2-bromoisobutyryloxy)ethyl methacrylate), and its structure was characterized by ~1H-NMR. This macroinitiator was used for ATRP of styrene to synthesize poly(methyl methacrylate)-graft-polystyrene. Themolecular weight of graft copolymer increased with the monomer conversion, and the polydispersity remained relatively low.The individual grafted polystyrene chains were cleaved from the macroinitiator backbone by hydrolysis and the hydrolyzed product was characterized by ~1H-NMR and GPC.
The radical copolymerization of methyl methacrylate and 2-hydroxyethyl methacrylate was carried out via atomtransfer radical polymerization (ATRP) initiated by ethyl 2-bromoisobutyrate and catalyzed by CuBr/2,2'-bipyridinecomplex. This polymerization proceeds in a living fashion with controlled molecular weight and low polydispersity. Theobtained copolymer was esterified with 2-bromoisobutylryl bromide yielding a macroinitiator, poly(methyl methacrylate-co-2-hydroxyethyl methacrylate-co-2-(2-bromoisobutyryloxy)ethyl methacrylate), and its structure was characterized by ~1H-NMR. This macroinitiator was used for ATRP of styrene to synthesize poly(methyl methacrylate)-graft-polystyrene. Themolecular weight of graft copolymer increased with the monomer conversion, and the polydispersity remained relatively low.The individual grafted polystyrene chains were cleaved from the macroinitiator backbone by hydrolysis and the hydrolyzed product was characterized by ~1H-NMR and GPC.
基金
This project was supported in part by the Ministry of Education of China (No. JG2000-11).