一种高吸水性树脂的制备

Preparation of a Super Absorbent Polymer

通过优化工艺配方制备出吸水倍率高、吸水速度快的高吸水性树脂材料。通过研究可知,中和度为75%,共聚单体用量为10%,交联剂用量为0.15%,引发剂用量为0.1%,表面处理助剂甘油用量为0.8%时,产品综合性能指标最优。

The super absorbent polymerl with high water absorption rate and high water absorption rate was prepared by optimizing the process.Through the study,the neutralization degree was 75%,the dosage of copolymer was 10%,the dosage of crosslinking agent was 0.15%,the dosage of initiator was 0.1%,and the content of surface treatment agent was 0.8%.