研究了微胶囊红磷对环氧树脂基电子电气封装材料的阻燃性能、力学性能及抑烟性能的影响。结果表明 :添加 10份微胶囊红磷即可使材料的阻燃性能达到UL 94V -0级 ,氧指数从 19 5 %上升到 2 8 2 % ;添加量在一定的范围内对材料的力学性能影响很小 ,添加量从 0增加至 14份时 ,材料的拉伸强度略有下降 ,冲击强度有所上升 ,弯曲强度略有上升后有所降低 ;微胶囊红磷与硼酸锌的复配体系具有很好的抑烟性能。
The effects of microencapsulated red phosphorus on the flame retardancy, mechanical properties and smoke suppression of epoxy resin packaging materials are studied in this paper The results showed when the material was flame-retarded with 10 phr of microencapsulated red phosphorus, the flame retardancy of the material came up to UL 94 V-0 level and the LOI came up from 19 5% to 28 2%; when the content of the microencapsulated red phosphorus was in a certain extent, its effect on the mechanical properties was small; when the content changed from 0 to 14 phr, the tensile strength decreased a little, but the impact strength increased and the bend strength increased at first and then decreased The composite system of microencapsulated red phosphorus with zinc borate had good smoke suppression on the material
出处
《塑料工业》
CAS
CSCD
北大核心
2003年第7期49-51,共3页
China Plastics Industry
关键词
微胶囊
红磷阻燃剂
环氧树脂基封装材料
硼酸锌
阻燃性能
Microencapsulated Red Phosphorus
Epoxy Resin Packaging Material
Zinc Borate
Flame Retardancy