This paper presents the results of the study concerning to the leakagecurrent behaviour on artificially polluted ceramic insulator surface. From the present study it wasobserved that there is a reasonably well-defined inception of current i.e. scintillations at afinite voltage, The corresponding voltages for extinction of the current are in the range of 0.8 kVto 2.1 kV. Obviously, the dry band formed in the immediate vicinity of the pin prevents smoothcurrent flow as the voltage rises from zero. Only when the voltage is adequate it causes a flashoverof the dry band and current starts flowing. As is common in similar current extinction phenomena,here also, the extinction voltages are significantly lower than the inception voltages. Further, thevoltage-current curves invariably show hysteresis - the leakage currents are lower in the reducingportion of the voltage. This is obviously due to drying of the wet pollutant layer therebyincreasing its resistance. It is believed that this is the first time that such a directquantitative evidence of drying in individual half cycles is experimentally visualized.
This paper presents the results of the study concerning to the leakagecurrent behaviour on artificially polluted ceramic insulator surface. From the present study it wasobserved that there is a reasonably well-defined inception of current i.e. scintillations at afinite voltage, The corresponding voltages for extinction of the current are in the range of 0.8 kVto 2.1 kV. Obviously, the dry band formed in the immediate vicinity of the pin prevents smoothcurrent flow as the voltage rises from zero. Only when the voltage is adequate it causes a flashoverof the dry band and current starts flowing. As is common in similar current extinction phenomena,here also, the extinction voltages are significantly lower than the inception voltages. Further, thevoltage-current curves invariably show hysteresis - the leakage currents are lower in the reducingportion of the voltage. This is obviously due to drying of the wet pollutant layer therebyincreasing its resistance. It is believed that this is the first time that such a directquantitative evidence of drying in individual half cycles is experimentally visualized.