The effect of chemical plating with Ni Co P alloy on the properties of MH electrodes is investigated. The results show that the efficiency of storage alloy and the activation of MH electrode have been improved by introducing 1.74% cobalt in the Ni Co P alloy coating. The initial discharge capacity is 208 mAh/g. The maximum discharge capacity gets to 298.5 mAh/g. At the same time the cycle life of MH electrodes is improved. The discharge capacity of MH electrodes coated with Ni Co P is 88% of the maximum discharge capacity after 300 cycles. Whereas the discharge capacity of bare alloy electrodes retains 62% of the maximum capacity after 300 cycles. An increment of discharge capacity is mainly due to the superposition of the oxidation current of Co as well as improved efficiency of microcurrent collection. The effect of Ni Co P alloy coating by electroless plating on the kinetic properties of hydride electrode has been systematically investigated by electrochemical techniques. The results indicate that the kinetic properties of MH electrodes, including exchange current density, limiting current density, have been improved markedly. This improvement of kinetic properties leads to the decrease of the overpotential of anodic and cathodic polarization.
The effect of chemical plating with Ni Co P alloy on the properties of MH electrodes is investigated. The results show that the efficiency of storage alloy and the activation of MH electrode have been improved by introducing 1.74% cobalt in the Ni Co P alloy coating. The initial discharge capacity is 208 mAh/g. The maximum discharge capacity gets to 298.5 mAh/g. At the same time the cycle life of MH electrodes is improved. The discharge capacity of MH electrodes coated with Ni Co P is 88% of the maximum discharge capacity after 300 cycles. Whereas the discharge capacity of bare alloy electrodes retains 62% of the maximum capacity after 300 cycles. An increment of discharge capacity is mainly due to the superposition of the oxidation current of Co as well as improved efficiency of microcurrent collection. The effect of Ni Co P alloy coating by electroless plating on the kinetic properties of hydride electrode has been systematically investigated by electrochemical techniques. The results indicate that the kinetic properties of MH electrodes, including exchange current density, limiting current density, have been improved markedly. This improvement of kinetic properties leads to the decrease of the overpotential of anodic and cathodic polarization.
出处
《中国有色金属学会会刊：英文版》
CSCD
2003年第4期938-942,共5页
Transactions of Nonferrous Metals Society of China
基金
Project (973 10 3 711)supportedbytheCommitteeofScienceandTechnologyofTianjin