摘要
Polymer nanoparticles were prepared in the methyl methacrylate (MMA)/buty lmethacrylate (BA) emulsion copolymerization process by a modified microemulsion copolymerization method. 2-Hydroxyethyl methacrylate(HEMA), acrylate (AA) and methyl acrylate (MAA) were used as reactive cosurfactants. With this process high polymer: surfactant weight ratios (40:1 or greater),relatively concentrated (~30wt. %) latexes and small (~60nm) particle diameters were obtained.Properties of the latexes were characterized by TEM, DSC, dynamic light scattering, and IR spectroscopy.
Polymer nanoparticles were prepared in the methyl methacrylate (MMA)/butyl methacrylate (BA) emulsion copolymerization process by a modified microemulsion copolymerization method. 2-Hydroxyethyl methacrylate(HEMA), acrylate (AA) and methyl acrylate (MAA) were used as reactive cosurfactants. With this process high polymer: surfactant weight ratios (40:1 or greater), relatively concentrated (~30wt. %) latexes and small (~60nm) particle diameters were obtained. Properties of the latexes were characterized by TEM, DSC, dynamic light scattering, and IR spectroscopy.
基金
CEM Foundation For N & T Joint Academy (Chinese Education Ministry Foundation for Nankai University and Tianjin University Joint Academy)