摘要
通过热压法制水泥刨花板的试验,研究了6种不同形态的刨花对快速固化水泥刨花板性能的影响。研究的固定工艺条件为:灰木比2 6,水灰比0 6,Na2SiO3为水泥质量的10%,板的设计密度为1250kg·m-3,热压温度90℃,热压时间15min,压力3 0MPa。结果表明:①6种形态的刨花中以E型薄片刨花为最好。②用热压法快速固化制水泥刨花板时,较佳的刨花尺寸为:20~40mm×2~4mm×0 2~0 4mm。
The effects of 6 different wood shaving shapes on the properties of fastcuring cement particle board(CPB)are studied with the method of hot pressing.The constant technical conditions for the study are as follows:cementwood ratio is 26;watercement ratio is 06;the content of Na2SiO3 is 10% of cement weight;the designed density of the board is 1 250 kg·m-3;hot pressing temperature is 90 ℃ for 15 min;pressure is 30 MPa.The results are as follows:(1)Eshaped shaving is the best of the six shavings.(2)When the CPB is cured fast with the hot pressing method,the optimum size of shaving is(20~40)mm×(2~4)mm×(02~04)mm.
出处
《浙江林学院学报》
CAS
CSCD
北大核心
2003年第3期236-239,共4页
Journal of Zhejiang Forestry College
基金
九五"浙江省科学技术厅重点资助项目(962102065)
关键词
水泥刨花板
刨花形态
热压法
快速固化
cement particle board
shaving shape
hot pressing
fast-curing