A new kind of plasma technology with both high deposition rate and low dilution ratio was developed under the calculation and analysis of the arc flame characteristics of plasma arc,the kinematics behavior of powder and powder's heating in the arc. Compared with normal plasma surfacing method, the idea using constricting nozzle with small orifice diameter, long plasma arc and increasing the distance from meeting point of the two beams of powder to workpiece, to achieve the goals of high deposition rate and low dilution ratio, was put forward here. In order to prove this idea, a set of experimental system was built up and obtained satisfied results including high deposition rate(more than 25 kg/h )and low dilution ratio(less than 5%). The success of this study offers a promising prospect for developing the powder plasma surface welding in China and may open a way to improve this technology further in efficiency and quality.
A new kind of plasma technology with both high deposition rate and low dilution ratio was developed under the calculation and analysis of the arc flame characteristics of plasma arc,the kinematics behavior of powder and powder's heating in the arc. Compared with normal plasma surfacing method, the idea using constricting nozzle with small orifice diameter, long plasma arc and increasing the distance from meeting point of the two beams of powder to workpiece, to achieve the goals of high deposition rate and low dilution ratio, was put forward here. In order to prove this idea, a set of experimental system was built up and obtained satisfied results including high deposition rate(more than 25 kg/h )and low dilution ratio(less than 5%). The success of this study offers a promising prospect for developing the powder plasma surface welding in China and may open a way to improve this technology further in efficiency and quality.