摘要
The experiments were carried out at 1 175-1 450 ℃ to study the phosphorus distribution ratio between molten Ca O-based slags and carbon saturated hot metal. The phosphate capacity of the slags and the activity coefficient of PO2. 5were calculated from the phosphorus distribution ratio. The effect of addition of Ca F2 and / or Ca Cl2 on the thermodynamic properties of slags was discussed. The correlation of optical basicity with phosphate capacity of slags was studied,and the dephosphorization ability of Ca O-based fluxes with various additives was compared with the results from different studies.
The experiments were carried out at 1 175-1 450 ℃ to study the phosphorus distribution ratio between molten Ca O-based slags and carbon saturated hot metal. The phosphate capacity of the slags and the activity coefficient of PO2. 5were calculated from the phosphorus distribution ratio. The effect of addition of Ca F2 and / or Ca Cl2 on the thermodynamic properties of slags was discussed. The correlation of optical basicity with phosphate capacity of slags was studied,and the dephosphorization ability of Ca O-based fluxes with various additives was compared with the results from different studies.