浅析商品混凝土碳化深度过大的原因

下载PDF

导出

摘要本文叙述了混凝土碳化深度的定义及危害,同时列举了影响混凝土碳化深度的因素,分析了商品混凝土碳化深度过大的原因,并提出了降低碳化深度的建议。

作者马晓华

机构地区河南省诚建工程质量检测有限公司

出处《四川水泥》 2014年第11期218-218,229,共2页 Sichuan Cement

关键词商品混凝土碳化二氧化碳氢氧化钙

参考文献2

1L. J. Parrott.Damage caused by carbonation of reinforced concrete[J]. Materials and Structures . 1990 (3)
2P.Sulapha,S.F.Wong,T.H.Wee,S.Swaddiwudhipong.Carbonation of concrete containing mineral admixtures. Journal of Materials in Civil Engineering (ASCE) . 2003
3Kritsada Sisomphon,Lutz Franke.Carbonation rates of concrete containing high volume of pozzolanic materials. Cement and Concrete Composites . 2007
4Claus Pade,Maria Guimaraes.The uptake of concrete in a 100 year perspective. Cement and Concrete Composites . 2007
5D.A.St John,A.B.Pook,I.Sims.Conrete Petrography. . 1998
6http://en.wikipedia.org/wiki/carbon_dioxide_in_Earth’’s_atmosphere .
7D.O.McPolin,P.A.M.Basheer,A.E.Long,K.T.V.Grattem,T.Sun.New test method to obtain pH profiles due to carbonation of concrete containing supplementary cementitious materials. Journal of Materials in Civil Engineering (ASCE) . 2007
8P.Castro,E.I.Mereno,J.Genesca.Influence of marine micro-climates on carbonation of reinforced concrete buildings. Cement and Concrete Composites . 2000
9C.T.Tam,,H.B.Lim,,K.Sisomphon.Carbonation of concrete in the tropical environment of Singapore. The IES Journal Part A:Civil and Structural Engineering . 2008
10Aron Beutur,Denis Mitchell.Materials performance lessons. Cement and Concrete Composites . 2008

1张文俊,刘保华,周文,赵志华,肖宏,叶煜飘,陈礼德.油菜秸秆纤维混凝土抗碳化性能的试验研究[J].湖南农业大学学报（自然科学版）,2021,47(1):96-100. 被引量：7
2刘巧玲,张文俊.温湿度对油菜秸秆混凝土抗碳化性影响试验研究[J].中阿科技论坛（中英文）,2021(10):88-90. 被引量：3
3龚小兵,廖方.地下管廊耐久性控制要点思考与建议[J].四川建筑,2019,39(1):116-117.

四川水泥

2014年第11期

内容加载中请稍等...