以羟基封端的聚二甲基硅氧烷为改性试剂、己内酰胺为封端剂、羧酸基多元醇做亲水扩链剂,采用阴离子自乳化的方法制备一种聚二甲基硅氧烷改性的环境友好型水性聚氨酯阻燃胶黏剂。通过傅里叶变换红外光谱仪(FT-IR)、万能试验机,极限氧指数测试仪等实验仪器对水性聚氨酯阻燃胶黏剂进行了阻燃性能和力学性能表征。研究结果表明,羟基封端的聚硅氧烷接入分子链结构中,合成的聚氨酯具有良好的阻燃效果,并且得到难燃的胶黏材料,表现出良好的阻燃与力学性能。
With Polydimethylsiloxane as modified reagent and caprolactam as a cappingagent and 2,2-Bis(hydroxymethyl)propionic acid(DMPA) as hydrophilic chain extender,the anion self-emulsifying method is adopted to prepare a kind of an environmental friendly waterborne polyurethane flame retardant adhesive.The waterborne polyurethane flame retardant adhesive was characterized by,fourier transform infared spectrometer(FT-IR),universal testing machine and other experimental instruments.Flame retardance was tested by limiting oxygen index(LOI)tester.The results show that the synthesized polyurethane has good flame retardant effect when hydroxyl terminated polysiloxane is inserted into the molecular chain structure,and the flame retardant adhesive material is obtained,showinggood flame retardant and mechanical properties.
作者
黄传峰
刘青青
闵钰茹
张丹丹
崔玮
夏其英
梁士明
马登学
Huang Chuanfeng;Liu Qingqing;Min Yuru;Zhang Dandan;Cui Wei;Xia Qiying;Liang Shiming;Ma Dengxue(School of Materials Science and Engineering,Linyi University,Linyi 276005,China;School of Chemistry and Chemical Engineering,Linyi University,Linyi 276005,China)
出处
《山东化工》
CAS
2019年第5期34-36,共3页
Shandong Chemical Industry
基金
国家大学生创新创业训练项目(编号:201810452066)
2018年山东省本科教改项目(加强科教融合
发挥学科优势
探索地方高校拔尖创新型人才培养新模式Z2018S006)
中国轻工业联合会教育工作分会2018年度课题(新工科背景下以科研项目为支撑的拔尖创新型人才培养模式研究QGJY2018041)
2016年临沂大学教改项目(以社会需求为导向的材料科学与工程专业创新人才培养模式改革研究)
2017年临沂大学教育信息化研究课程(高分子化学实验)
2017年临沂大学学生学习评价改革课程(高分子物理实验)
关键词
水性聚氨酯
阻燃
改性
有机硅
胶黏剂
waterborne polyurethane
self emulsification
modified
adhesive
flame retardant