摘要
LiMn 2O 4-x F x prepared by the sol gel method has a perfect crystal formation .The crystal particle size of the material was medium and distributed uniformly. The substitution of F for O increased the specific capacity of the material at the cost of the cycleability .The explanation of this results is that the F decreases the valence of Mn,that is,more Mn 3+ and less Mn 4+ exist in the material.The increase of Mn 3+ will improve the initial specific capacity and Mn 3+ is the original reason for Jahn Teller effect that caused the poor cycleability of the cathode material by the micro distortion of the crystal structure. In addition, the expanded measurement of the crystal lattice is also the reason for the poor cycleability.Therefore,the results of F substitution and cation substitution are opposite.If the two methods are combined,they can compensate the inability each other and the satisfactory results may be obtained.
LiMn 2O 4-x F x prepared by the sol gel method has a perfect crystal formation .The crystal particle size of the material was medium and distributed uniformly. The substitution of F for O increased the specific capacity of the material at the cost of the cycleability .The explanation of this results is that the F decreases the valence of Mn,that is,more Mn 3+ and less Mn 4+ exist in the material.The increase of Mn 3+ will improve the initial specific capacity and Mn 3+ is the original reason for Jahn Teller effect that caused the poor cycleability of the cathode material by the micro distortion of the crystal structure. In addition, the expanded measurement of the crystal lattice is also the reason for the poor cycleability.Therefore,the results of F substitution and cation substitution are opposite.If the two methods are combined,they can compensate the inability each other and the satisfactory results may be obtained.
基金
FundedbytheNationalNaturalScienceFoundationofChina(No.5 9972 0 2 6 )