摘要
用 Czochralski 技术生长了 A 位置非充满型 KNSBN 掺 Cu 晶体,提拉速度为4—8mm/h,转速为15—20r/min;沿提拉方向测量了温场分布,用氩离子激光器测量了晶体的高光折变性能。
The unfully filled A-sites Cu-doped KNSBN crystal has beengrown by Czochralski technique.The pulling rate is 4-8mm/h,and the rotationrate 15-20r/min.The temperature field was measured along pulling directionThe high photorefractive properties have also been measured using Argon-ionlaser.
出处
《人工晶体学报》
EI
CAS
CSCD
1992年第2期110-113,共4页
Journal of Synthetic Crystals
基金
国家高技术发展计划新材料领域资助