A finite element(FE) model for the numerical control(NC) bending of Ti-3 Al-2.5 V titanium alloy seamless tube is established, considering the variation in the contractile strain ratio(CSR) and elastic modulus(E). The wall thinning characteristics of Ti-3 Al-2.5 V tube under different geometric and process conditions were investigated. The results showed that the CSR-E variation can change the wall thickness, but has no remarkable effect on the change characteristics. The reasonable parameter ranges are as follows: a bending-radius range not less than 1.5 times the outer diameter, a bend angle up to 180?, and a mandrel extension of 0-3 mm. The friction coefficient between the pressure die and the tube should be in the range of 0.20-0.35, and between the bending die and the tube should be in the range of 0.05-0.15. As long as the performance meets the requirements, the relative push-assistant speed should be as small as possible.
A finite element(FE) model for the numerical control(NC) bending of Ti-3 Al-2.5 V titanium alloy seamless tube is established, considering the variation in the contractile strain ratio(CSR) and elastic modulus(E). The wall thinning characteristics of Ti-3 Al-2.5 V tube under different geometric and process conditions were investigated. The results showed that the CSR-E variation can change the wall thickness, but has no remarkable effect on the change characteristics. The reasonable parameter ranges are as follows: a bending-radius range not less than 1.5 times the outer diameter, a bend angle up to 180?, and a mandrel extension of 0-3 mm. The friction coefficient between the pressure die and the tube should be in the range of 0.20-0.35, and between the bending die and the tube should be in the range of 0.05-0.15. As long as the performance meets the requirements, the relative push-assistant speed should be as small as possible.
作者
皇涛
王锟
詹梅
郭俊卿
陈学文
陈拂晓
宋克兴
HUANG Tao;WANG Kun;ZHAN Mei;GUO Junqing;CHEN Xuewen;CHEN Fuxiao;SONG Kexing
基金
the China Postdoctoral Science Foundation(No.2016M590677)
the National Natural Science Foundation of China(No.51741503)
the Fund of the State Key Laboratory of Solidification Processing in NWPU(No.SKLSP201631)
the Basic and Advanced Technology Research Program of Henan Province(No.162300410211)