摘要
Several acid compounds have been employed as additives of the V(V) electrolyte for vanadium redox flow battery(VRB) to improve its stability and electrochemical activity. Stability of the V(V) electrolyte with and without additives was investigated with ex-situ heating/cooling treatment at a wide temperature range of-5 ?C to 60 ?C. It was observed that methanesulfonic acid, boric acid, hydrochloric acid, trifluoroacetic acid,polyacrylic acid, oxalic acid, methacrylic acid and phosphotungstic acid could improve the stability of the V(V) electrolyte at a certain range of temperature. Their electrochemical behaviors in the V(V) electrolyte were further studied by cyclic voltammetry(CV), steady state polarization and electrochemical impedance spectroscopy(EIS). The results showed that the electrochemical activity, including the reversibility of electrode reaction, the diffusivity of V(V) species, the polarization resistance and the flexibility of charge transfer for the V(V) electrolyte with these additives were all improved compared with the pristine solution.
Several acid compounds have been employed as additives of the V(V) electrolyte for vanadium redox flow battery(VRB) to improve its stability and electrochemical activity. Stability of the V(V) electrolyte with and without additives was investigated with ex-situ heating/cooling treatment at a wide temperature range of-5 ?C to 60 ?C. It was observed that methanesulfonic acid, boric acid, hydrochloric acid, trifluoroacetic acid,polyacrylic acid, oxalic acid, methacrylic acid and phosphotungstic acid could improve the stability of the V(V) electrolyte at a certain range of temperature. Their electrochemical behaviors in the V(V) electrolyte were further studied by cyclic voltammetry(CV), steady state polarization and electrochemical impedance spectroscopy(EIS). The results showed that the electrochemical activity, including the reversibility of electrode reaction, the diffusivity of V(V) species, the polarization resistance and the flexibility of charge transfer for the V(V) electrolyte with these additives were all improved compared with the pristine solution.
基金
supported by the Doctoral Program of Higher Education(No.20110181110003)
the Collaborative innovation fund by China Academyof Engineering Physics and Sichuan University(No.XTCX2011001)
the Sichuan Provincial Department of Science and Technology R&D Program(No.2013FZ0034)