We have developed a Si/graphene oxide electrode synthesized via ultrasonication-stirring method under alkaline condition. Scanning electron microscopy(SEM), transmission electron microscope(TEM), EDS dot-mapping and high-resolution transmission electron microscopy(HRTEM) results show that Si particles are evenly dispersed on the graphene oxide sheets. The electrochemical performance was investigated by galvanostatic charge/discharge tests at room temperature. The results revealed that Si/graphene oxide electrode exhibited a high reversible capacity of 2825 mAh/g with a coulombic efficiency of 94.6%at 100 mA/g after 15 cycles and a capacity retention of 70.8% after 105 cycles at 4000 mA/g. These performance parameters show a great potential in the high-performance batteries application for portable electronics, electric vehicles and renewable energy storage.
We have developed a Si/graphene oxide electrode synthesized via ultrasonication-stirring method under alkaline condition. Scanning electron microscopy(SEM), transmission electron microscope(TEM), EDS dot-mapping and high-resolution transmission electron microscopy(HRTEM) results show that Si particles are evenly dispersed on the graphene oxide sheets. The electrochemical performance was investigated by galvanostatic charge/discharge tests at room temperature. The results revealed that Si/graphene oxide electrode exhibited a high reversible capacity of 2825 mAh/g with a coulombic efficiency of 94.6%at 100 mA/g after 15 cycles and a capacity retention of 70.8% after 105 cycles at 4000 mA/g. These performance parameters show a great potential in the high-performance batteries application for portable electronics, electric vehicles and renewable energy storage.
基金
the financial support from National Basic Research Program of China (973 program no. 2013CB934700)