Pure WO_3 and Yb:WO_3 thin films have been synthesized by spray pyrolysis technique. Effect of Yb doping concentration on photoelectrochemical, structural, morphological and optical properties of thin films are studied. X-ray diffraction analysis shows that all thin films are polycrystalline nature and exhibit monoclinic crystal structure. The 3 at% Yb:WO_3 film shows superior photoelectrochemical(PEC) performance than that of pure WO_3 film and it shows maximum photocurrent density(Iph= 1090 μA/cm^2) having onset potentials around +0.3 V/SCE in 0.01 M HClO_4. The photoelectrocatalytic process is more effective than that of the photocatalytic process for degradation of methyl orange(MO) dye. Yb doping in WO_3 photocatalyst is greatly effective to degrade MO dye. The enhancement in photoelectrocatalytic activity is mainly due to the suppressing the recombination rate of photogenerated electron-hole pairs. The mineralization of MO dye in aqueous solution is studied by measuring chemical oxygen demand(COD) values.
Pure WO_3 and Yb:WO_3 thin films have been synthesized by spray pyrolysis technique. Effect of Yb doping concentration on photoelectrochemical, structural, morphological and optical properties of thin films are studied. X-ray diffraction analysis shows that all thin films are polycrystalline nature and exhibit monoclinic crystal structure. The 3 at% Yb:WO_3 film shows superior photoelectrochemical(PEC) performance than that of pure WO_3 film and it shows maximum photocurrent density(Iph= 1090 μA/cm^2) having onset potentials around +0.3 V/SCE in 0.01 M HClO_4. The photoelectrocatalytic process is more effective than that of the photocatalytic process for degradation of methyl orange(MO) dye. Yb doping in WO_3 photocatalyst is greatly effective to degrade MO dye. The enhancement in photoelectrocatalytic activity is mainly due to the suppressing the recombination rate of photogenerated electron-hole pairs. The mineralization of MO dye in aqueous solution is studied by measuring chemical oxygen demand(COD) values.
基金
University Grants Commission(UGC),New Delhi,for the financial support through the project No.‘‘41-869/2012(SR)’’