摘要
The aging precipitation behavior of beta phase in two kinds of alloys with7/3 and 9/1 ssickel4o-iron ratios during aging at 800 deg C after deformation was studied. Theresults show that there are two different kinds of aging hardness variation mechanisms (thesoftening mechanism and the hardening mechanism) deciding the hardness variations of the alloys.when Ni/Fe is smaller than8/2, there is only the softening mechanism which results from the decreasing of dislocation densityand recovery or re-crystallization. And when NI/Fe is greater than 8/2 besides the softeningmechanism there is still the hardening mechanism that is induced by the precipitation of beta phase.
The aging precipitation behavior of beta phase in two kinds of alloys with7/3 and 9/1 ssickel4o-iron ratios during aging at 800 deg C after deformation was studied. Theresults show that there are two different kinds of aging hardness variation mechanisms (thesoftening mechanism and the hardening mechanism) deciding the hardness variations of the alloys.when Ni/Fe is smaller than8/2, there is only the softening mechanism which results from the decreasing of dislocation densityand recovery or re-crystallization. And when NI/Fe is greater than 8/2 besides the softeningmechanism there is still the hardening mechanism that is induced by the precipitation of beta phase.
基金
National Natural Science Foundation of China (No.59971007)