Acrylic acid was graft-copolymerized onto Rhi. oryzae's cell wall structural polysaccharide directly and efficiently in aqueous solution with eerie ammonium nitrate as initiator. The maximal grafting percentage of 135.5% was obtained under the condition of [Ce4+]=5mmol·L-1, [AA]=lmol·L-1, T=60℃ and t=3h. Graft copolymerization was suggested to proceed through free radical reaction mechanism. Grafting occurred primarily on chitosan. Acrylic acid was also attempted to be grafted onto Asp. niger cell wall structural polysaccharide, and only 44.2% of grafting percentage was resulted.
Acrylic acid was graft-copolymerized onto Rhi. oryzae's cell wall structural polysacchaxide directly and efficiently in aqueous solution with ceric ammonium nitrate as initiator. The maximal grafting percentage of 135.5％ was obtained under the condition of [Ce4+]＝5mmol.L-1, [AA]=1mol.L-1, T＝60°C and t＝3h. Graft copolymerization was suggested to proceed through free radical reaction mechanism. Grafting occurred primarily on chitosan. Acrylic acid was also attempted to be grafted onto Asp. niger cell wall structural polysaccharide, and only 44.2％ of grafting percentage was resulted.
基金
the National Natural Science Foundation of China (No. 29606009).