The sorption behavior of amino methylene phosphonic acid resin (APAR) for In (Ⅲ ) was investigated . Experimental results show that In ( Ⅲ ) adsorbed on APAR can be elated with 2mol · L -1 HCl. The apparent rate constant is k29 = 1.50 × 10-5s-1. The sorption behavior of APAR for In ( Ⅲ ) obeys the Freundlich isotherm. The themodynamic parameters of sorption, enthalpy change ()H, free energy change ()G and entropy change ()S of sorption (APAR) for In ( Ⅲ ) are 24.1 kJ·mol-1, -35. 1kJ· mol-1 and 200J· mol-1·K-1 respectively. The coordination molar ratio of the functional group of APAR to In( Ⅲ ) is 2:1. The sorption mechanism of APAR for In( Ⅲ ) was examined by IR spectrometry.
The sorption behavior of amino methylene phosphonic acid resin (APAR) for In (Ⅲ ) was investigated . Experimental results show that In ( Ⅲ ) adsorbed on APAR can be elated with 2mol · L -1 HCl. The apparent rate constant is k29 = 1.50 × 10-5s-1. The sorption behavior of APAR for In ( Ⅲ ) obeys the Freundlich isotherm. The themodynamic parameters of sorption, enthalpy change ()H, free energy change ()G and entropy change ()S of sorption (APAR) for In ( Ⅲ ) are 24.1 kJ·mol-1, -35. 1kJ· mol-1 and 200J· mol-1·K-1 respectively. The coordination molar ratio of the functional group of APAR to In( Ⅲ ) is 2:1. The sorption mechanism of APAR for In( Ⅲ ) was examined by IR spectrometry.
基金
This project was supported by Foundation of Zhejiang Provincial Education Bureau(No.20010677) and Lishui Science and Technology Bureau(No.2001012)