By using self-made metal-alkoxide yttrium isopropoxide as a sintering additive and disperser of whisker, the SiC whisker reinforced AIN ceramics was prepared. Its apparent density is 99.5 percent of the theoretical density; its flexural strength and fracture toughness are 681 MPa and 5.21 MPa·m1/2 respectively. Comparing the result with that by applying Y2O3 powder as a sintering additive, the flexural strength is increased by 25% and the fracture toughness is increased by 33% . The dispersity of whisker by increased yttrium isopropoxide is significantly better than that by Triton X-100.
By using self-made metal-alkoxide yttrium isopropoxide as a sintering additive and disperser of whisker, the SiC whisker reinforced AIN ceramics was prepared. Its apparent density is 99.5 percent of the theoretical density; its flexural strength and fracture toughness are 681 MPa and 5.21 MPa·m1/2 respectively. Comparing the result with that by applying Y2O3 powder as a sintering additive, the flexural strength is increased by 25% and the fracture toughness is increased by 33% . The dispersity of whisker by increased yttrium isopropoxide is significantly better than that by Triton X-100.