The adsorption behavior and mechanism of a novel thiol resin for Ag(Ⅰ) were investigated Experimental results showed that the statically saturated sorption capacity was 639 mg·g -1 resin at pH=4 5 in the HNO 3 NaAc medium Ag(Ⅰ) adsorbed on the thiol resin could be eluted with (5%~10%) (NH 2) 2CS-1 0mol·L -1 HCl and elution percentage was over 95% The resin could be regenerated and reused without apparent decrease of adsorption capacity The adsorption behavior obeyed the Freundlich isotherm The apparent adsorption rate constant was k 25℃ =1 56×10 -5 s -1 The enthalpy change Δ H of sorption was 40 2 kJ·mol -1 The functional group molar ratio to Ag(Ⅰ) was about 1∶1 and the mechanism of adsorption was examined by IR
The adsorption behavior and mechanism of a novel thiol-resin for Ag(I) were investigated. Experimental results showed that the statically saturated sorption capacity was 639 mg·g-1 resin at pH=4.5 in the HNO3-NaAc medium. Ag(I) adsorbed on the thiol-resin could be eluted with (5%-10%)(NH2)2CS-1.0 mg·g-1 HC1 and elution percentage was over 95%. The resin could be regenerated and reused without apparent decrease of adsorption capacity. The adsorption behavior obeyed the Freundlich isotherm. The apparent adsorption rate constant was k25°C=1.56×10-5s-1. The enthalpy change AH of sorption was 40.2 mg·g-1. The functional group molar ratio to Ag(I) was about 1:1 and the mechanism of adsorption was examined by IR spectrometry.
出处
《化工学报》
EI
CAS
CSCD
北大核心
2003年第10期1466-1469,共4页
CIESC Journal
基金
浙江省高校中青年学科带头人基金
浙江省自然科学基金资助项目(No 2 0 0 0 72 )~~
关键词
巯基树脂
银
吸附
机理
Adsorption
Adsorption isotherms
Infrared spectroscopy
Silver