掺防冻剂混凝土钢筋阻锈机理的研究 被引量:1

MECHANISM OF CORROSION RESISTANT OF REINFORCING STEEL BARS OF CONCRETE WITH ANTI-FREEZING ADMIXTURE
下载PDF
导出
摘要 阐述了含不同浓度氯盐及亚硝酸盐防冻剂的砂浆,经水化后砂浆孔溶液中各种离子的浓度随着养护时间所发生的变化,并测定埋入钢筋的电极电位、钢筋腐蚀面积率、钢筋腐蚀减量等。实验结果表明:钢筋腐蚀时的电极电位、钢筋腐蚀面积率、钢筋腐蚀减量等性能与砂浆孔溶液中的离子浓度有密切的联系;掺入的NO_2^-浓度越大,硬化砂浆细孔溶液中的NO_2与Cl^-的摩尔比也越大,抑制钢筋腐蚀的效果越明显。 The experimental results are presented on the corrosion of reinforcing steel bars in the pore solutions of harden con-crete mortar with various anti-freezing admixtures with different concentrations of nitrite and chloride. The half-cell potentials, mass loss and corroded area of the reinforcing bars in the corrosion were measured for determination of the relationship between the ion concentration in the pore solution and the inhibition of corrosion. It is indicated that a higher nitrite content is, the high-er molar ratio of NO2-/Cl- is in pore solution, and the effective protection for the bars from corrosion in the mortar will be.
出处 《硅酸盐学报》 EI CAS CSCD 北大核心 2003年第11期1026-1030,共5页 Journal of The Chinese Ceramic Society
基金 国家自然科学基金(50078019) 国家留学基金 哈尔滨工业大学交叉学科基金(HIT MD2001.10)。
关键词 混凝土 钢筋腐蚀 防冻剂 孔溶液 阻锈机理 concrete steel corrosion anti-freezing admixture pore solution corrosion resistant
  • 相关文献

参考文献2

  • 1..コンクリ-ト构造物の腐食.防食にvする试验方法ならびに规(案)[S].コンクリ-ト工学协会,..
  • 2岸谷孝一他.c害(Ⅰ)[M].日本:技报堂出版,1986.32.

同被引文献11

  • 1柳俊哲,冯奇,李玉顺.混凝土中钢筋宏电池腐蚀电流的研究[J].建筑材料学报,2005,8(1):90-93. 被引量:10
  • 2ZITROU E, NIKOLAOU J, TSAKIRIDIS P E. Atmospheric corrosion of steel reinforcing bars produced by various manufacturing process [J].Construct Build Mater, 2007, 21 (6): 1161-1169.
  • 3李翰承.腐食劣化した鉄筋コンクリ-ト構造物の耐力性能評価ぉょび補強に関する研究[D].東京大学博士学位論文,1997:78-89.
  • 4ASTMC 876-91. Half cell potentials of reinforcing steel in concrete [S]. 1991.
  • 5日本コンクリ-ト工学協会. コンクリ-ト構造物の腐食防食に関する試験方法をらひに规準(案)[S].1997:7-9.
  • 6日本建築学会.鉄筋コンクリ-ト造建築物の耐久性調查·診斷ぉゅひ補修指針(案)·同解說[S].1997:6.
  • 7SONG H W, LEE C H, ANN K Y. Factors influencing chloride transport in concrete structures exposed to marine environments [J]. Cem Concr Compos, 2008, 30(2): 113-121.
  • 8CHANG Zhentian, CHERRY Brian. Polarization behavior of steel bar samples in concrete in seawater. Part 1 : Experimental measurement of polarization curves of steel in concrete [J]. Corros Sci, 2008, 50: 357-364.
  • 9宋晓冰,孔启明,刘西拉.普通硅酸盐混凝土中临界氯离子浓度的试验研究[J].土木工程学报,2007,40(11):59-63. 被引量:25
  • 10柳俊哲,巴恒静.亚硝酸根在混凝土中扩散及防锈年限预测[J].武汉理工大学学报,2003,25(10):39-42. 被引量:20

引证文献1

二级引证文献15

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部