摘要
Ternary metals disulfide nano-compound, Mn x(MoW) 1-xS 2, was prepared by exfoliating-restacking-structure controlling approach, and characterized by XRD, TEM, SAED and EDS respectively. XRD results show that the phases of the intermediate were composed of MoS 2, WS 2, MnCl 2·H 2O and one unclear phase. The end product was composed of MnS 2, MoS 2 and WS 2 phases. TEM results show that the morphologies of the sample are nano-tubular with ringent. EDS results show that the components of nanotube is Mn x(MoW) 1-xS 2. More detailed work is needed to study the precise structure and formation mechanism for sure.
Ternary metals disulfide nano-compound, Mn x(MoW) 1-xS 2, was prepared by exfoliating-restacking-structure controlling approach, and characterized by XRD, TEM, SAED and EDS respectively. XRD results show that the phases of the intermediate were composed of MoS 2, WS 2, MnCl 2·H 2O and one unclear phase. The end product was composed of MnS 2, MoS 2 and WS 2 phases. TEM results show that the morphologies of the sample are nano-tubular with ringent. EDS results show that the components of nanotube is Mn x(MoW) 1-xS 2. More detailed work is needed to study the precise structure and formation mechanism for sure.
出处
《高等学校化学学报》
SCIE
EI
CAS
CSCD
北大核心
2003年第12期2155-2157,共3页
Chemical Journal of Chinese Universities
基金
国家自然科学基金 (批准号 :2 0 1710 3 9
5 0 1710 63 )资助