摘要
Water soluble conducting polyaniline with electrical conductivity of 10^(-1)-10^(-2) S/cm was prepared employingdopant induced water solubility technology. The water resistance of the conducting film was significantly improvedemploying sol-gel hybrids method, especially when the conductive polyaniline loading was below 30 wt%. The reason forthe improvement is that the conducting polyaniline chains are confined in a stable inorganic network.
Water soluble conducting polyaniline with electrical conductivity of 10^(-1)-10^(-2) S/cm was prepared employingdopant induced water solubility technology. The water resistance of the conducting film was significantly improvedemploying sol-gel hybrids method, especially when the conductive polyaniline loading was below 30 wt%. The reason forthe improvement is that the conducting polyaniline chains are confined in a stable inorganic network.