摘要
研究了均匀化温度、热轧道次改变对 3 10 4制罐板化合物形态的影响。试验结果表明 ,3 10 4制罐板铸锭 580 ℃ ,15h均匀化热轧三道次工艺生产的成品板化合物破碎更充分 ,分布均匀、弥散。
The effect of homogenization temperature and hot rolling pass change on the compound morphology of 3104 sheet used for can was studied The result shows that the compound in finished sheet made by 3104 alloy can stock homogenized at 580℃ for 15h and hot rolled in 3 pass were fully broken, evenly distributed and dispersed
出处
《铝加工》
CAS
2003年第6期25-28,31,共5页
Aluminium Fabrication