水煤浆气化炉用氧化铬砖的蚀变
摘要
采用SEM、EDAX和XRD方法研究了水煤浆气化炉用后的烧结氧化铬砖的蚀变机理。反映在显微结构上的变化为：1)玻璃相数量增多且其组成各异；2)形成二次锆英石；3)Cr2O3和α—Al2O3之间形成(Al2-x，Crx)O3固溶体。侵蚀机理主要是渗入的液相离解晶间和粒间的结合并冲蚀。
出处
《耐火材料》
CAS
北大核心
2003年第G00期96-101,共6页
Refractories
参考文献7
-
1Schultz A H, Smbican V. Separation of Phaaes by spinodal decomposition in the systems Al2O3 - Cr2O3 and Al2O3 - Cr2O3 - Fe2O3. J Am Ceram Soc,1970,11:613 -616.
-
2Bondioli F,Ferrayi A M,Linati L. Reaction mechanism in aluminachromia( Al2O3 - Cr2O3 ) solid soluliom obtained by copmcipitation. ibid,2000 ,8 :2036 -2040.
-
3Lossi L R,Lawrence W G. Elastic properties of oxide solid solution :The system Al2O3 -Cr203. ibid,1970,11:604 -608.
-
4Ownby P D,Jungquist G E. Final sintefing of Cr2O3,J Am Ceram Soc,1971,55(9) :433 -436.
-
5Graham H C,Davis H H. Oxidation - vaporization kinetics of Cr2O3. J Am Ceram Soc,1972,54(2) :89 -93.
-
6Yamaguchi A. Grain growth during sintering of Cr2O3. J Ceram Soc Japan,1979,87(5) :253 -258.
-
7Yamaguchi A. Sintering of composition in the system Al2O3 - Cr2O3- SiO2. Ceramics International, 1986,12:19 - 24.
-
1王立群,王跃琪.水煤气炉粉煤制气技术及其应用[J].小氮肥,1998(2):11-12.
-
2刘会林.新型无铬耐火材料的试验评价[J].耐火与石灰,2016,41(2):43-47.
-
3曹海洁,李丽萍,徐晓莹.高铬砖中氧化锆含量的测定[J].分析化学,2009,37(A01):69-69.
-
4鲍礼堂,徐京磐,宋学武,靳希宏.循环流化床水煤气炉示范工程运行初步总结[J].小氮肥,2005,33(3):1-4. 被引量：1
-
5杨献斌,赵玉珠,王宗立,李学军,郭学群,尚守稳.Φ3.6m水煤气炉系统技术改造[J].煤化工,1999,27(4):43-44.
-
6李家振.Φ2260水煤气炉连续发生热混合煤气用于玻璃池炉熔制的改造[J].中国照明电器,2000(11):18-18.
-
7张周明,印杰,马旭峰,惠先磊,王群伟.高铬砖抗浮法玻璃侵蚀的研究[J].玻璃,2006,33(3):10-13.
-
8贾章林.气化炉炉底爆炸喷火原因分析[J].煤气与热力,2005,25(12):68-68. 被引量：1
-
9何旭远.电熔AZS蚀变与玻璃结石缺陷[J].中国玻璃,2011(1):19-23. 被引量：1
-
10敖进清,李楠,韩兵强.含钒钢渣对镁碳砖的侵蚀[J].耐火材料,2006,40(4):287-290. 被引量：9