Several indium borophosphates have been reported recently,including K In[BP 2 O 8 (OH)]( Ⅰ )and NaIn[BP 2 O 8 (OH)]( Ⅱ ).The latter two compounds were synthesized under mild hydrothermal condit ions,and have the same molar ratio(M Ⅰ ∶In∶B∶P∶O∶H)in molecular formula but with different structure types.C ompound Ⅰ crystallizes in the triclinic system with space group P1(No.2), a =0.52638(4)nm, b =0.84791(5)nm, c =0.81469(9)nm,α=91.1741(7)°,β=93.061(7) °,γ=79.823(5)°, V =0.3573nm 3 ,Z=2;while compound Ⅱ possesses a monoclinic structure with space group P 2 1 / n (No.14)with a =0.5177(1)nm, b =1.6815(3)nm, c =0.7684(2)nm,β=94.10(3)°, V =0.6672(2)nm 3 ,Z=4.Eight-membered-ring and six-membered-ring are formed by alterna ting borate,phosphate tetrahedra and In-coordination octahedron sharing corner s via common oxygen atoms in compound Ⅰ and Ⅱ respectively.The polyhedra in the structure are oriented along certain dire ction to form alternating layered fragments.These two structure types can be co nsidered as intergrowth structures,which consist of the same layered fragments growing in different orientations.Other structure intergrowth possibilities are also expected in similar systems.CSD: Ⅰ ,409583; Ⅱ ,413343.
Several indium borophosphates have been reported recently,including K In[BP 2 O 8 (OH)]( Ⅰ )and NaIn[BP 2 O 8 (OH)]( Ⅱ ).The latter two compounds were synthesized under mild hydrothermal condit ions,and have the same molar ratio(M Ⅰ ∶In∶B∶P∶O∶H)in molecular formula but with different structure types.C ompound Ⅰ crystallizes in the triclinic system with space group P1(No.2), a =0.52638(4)nm, b =0.84791(5)nm, c =0.81469(9)nm,α=91.1741(7)°,β=93.061(7) °,γ=79.823(5)°, V =0.3573nm 3 ,Z=2;while compound Ⅱ possesses a monoclinic structure with space group P 2 1 / n (No.14)with a =0.5177(1)nm, b =1.6815(3)nm, c =0.7684(2)nm,β=94.10(3)°, V =0.6672(2)nm 3 ,Z=4.Eight-membered-ring and six-membered-ring are formed by alterna ting borate,phosphate tetrahedra and In-coordination octahedron sharing corner s via common oxygen atoms in compound Ⅰ and Ⅱ respectively.The polyhedra in the structure are oriented along certain dire ction to form alternating layered fragments.These two structure types can be co nsidered as intergrowth structures,which consist of the same layered fragments growing in different orientations.Other structure intergrowth possibilities are also expected in similar systems.CSD: Ⅰ ,409583; Ⅱ ,413343.
出处
《无机化学学报》
SCIE
CAS
CSCD
北大核心
2004年第1期53-56,共4页
Chinese Journal of Inorganic Chemistry
基金
国家杰出 青年基金项目(No.20025101)
国家科技部863项目(No.2002AA324 070)
上海市光科技项目(No.022