A precursor of BaCe 0.9 Nd 0.1 O 3-δ solid electrolyte was synthesized by the sol-gel method and sintered at14 00℃.The obtained gels and powder were characterized by differential and ther mogravimetric thermal analysis(TG-DTA),X-ray diffraction(XRD),transmissi on electron microscopy(TEM).Using the sintered samples as solid electrolyte a nd silver-palladium alloy as electrodes,electrical conductivities under differ ent gas ambiences at intermediate temperature(400～600℃)were measured. In moist hydrogen atmosphere,the conduction is a little higher than that of dry hydrogen atmosphere.In hydrogen atmosphere,proton conduction may predominate ,leading to an increase in conductivity and a decrease in activation energy.
A precursor of BaCe 0.9 Nd 0.1 O 3-δ solid electrolyte was synthesized by the sol-gel method and sintered at14 00℃.The obtained gels and powder were characterized by differential and ther mogravimetric thermal analysis(TG-DTA),X-ray diffraction(XRD),transmissi on electron microscopy(TEM).Using the sintered samples as solid electrolyte a nd silver-palladium alloy as electrodes,electrical conductivities under differ ent gas ambiences at intermediate temperature(400～600℃)were measured. In moist hydrogen atmosphere,the conduction is a little higher than that of dry hydrogen atmosphere.In hydrogen atmosphere,proton conduction may predominate ,leading to an increase in conductivity and a decrease in activation energy.
出处
《无机化学学报》
SCIE
CAS
CSCD
北大核心
2004年第1期57-60,共4页
Chinese Journal of Inorganic Chemistry