The crystallization behavior of desulfurization product is directly related to its high-temperature-resistant ability.Effects of the additive on the sulfur-fixation efficiency of the Ba-sulfur-fixation agent and also on the crystallization behavior of the sulfur-fixation product were studied when CaCO 3 and BaCO 3 were used as the desulfurization agent and MgO and SrCO 3 used as the assistant sulfur-fixation agent. The result shows that increase of sulfur-fixation capability for the additive is not owe to their directly react to form sulfate or interact with CaCO 3 and BaCO 3 to form composite mineral heat-resistant in high temperature, but owe to their activation to sulfur-fixation reaction of the sulfur-fixation agent.
The crystallization behavior of desulfurization product is directly related to its high-temperature-resistant ability.Effects of the additive on the sulfur-fixation efficiency of the Ba-sulfur-fixation agent and also on the crystallization behavior of the sulfur-fixation product were studied when CaCO 3 and BaCO 3 were used as the desulfurization agent and MgO and SrCO 3 used as the assistant sulfur-fixation agent. The result shows that increase of sulfur-fixation capability for the additive is not owe to their directly react to form sulfate or interact with CaCO 3 and BaCO 3 to form composite mineral heat-resistant in high temperature, but owe to their activation to sulfur-fixation reaction of the sulfur-fixation agent.
基金
FundedbytheNationalNaturalScienceFoundationofChi na (No .5 0 2 76 0 4 5 )
DoctoralSubjectFoundationofChina (No.2 0 0 10 4 870 11)
andPostdoctorFoundationofChina (No.0 10 6 12 10 0 2 )