摘要
La0.9Sr0.1Ga0.8Mg0.2O3-δ（LSGM） and La0.7Sr0.3Cr0.5Mn0.5O3-δ（LSCM） powders were synthesized by glycine-nitrate process, and LSGM electrolyte thin film was successfully fabricated on porous anode substrate of LSCM by slurry spin coating technology. Some technical parameters for the preparation of LSGM thin films were systematically investigated, including ink composition,sintering temperature, and spin coating times. The electrolyte films with the best compactness and somewhat rough are obtained when the operating parameters are fixed as follows: the content of ethyl cellulose as binder is 5 wt%, the content of terpineol as modifier is 5 wt%, the optimum coating cycle number is 9 times, and the best post-deposition sintering temperature is 1,400 °C for 4 h.
La0.9Sr0.1Ga0.8Mg0.2O3-δ（LSGM） and La0.7Sr0.3Cr0.5Mn0.5O3-δ（LSCM） powders were synthesized by glycine-nitrate process, and LSGM electrolyte thin film was successfully fabricated on porous anode substrate of LSCM by slurry spin coating technology. Some technical parameters for the preparation of LSGM thin films were systematically investigated, including ink composition,sintering temperature, and spin coating times. The electrolyte films with the best compactness and somewhat rough are obtained when the operating parameters are fixed as follows: the content of ethyl cellulose as binder is 5 wt%, the content of terpineol as modifier is 5 wt%, the optimum coating cycle number is 9 times, and the best post-deposition sintering temperature is 1,400 °C for 4 h.
基金
financially supported by the National Natural Science Foundation of China (Nos. 51362011 and 51362012)
the Chemistry Discipline Master’s Site Construction Open Foundation of Honghe University of Yunnan Province (No. HXZ1308)