SmConanoparticles(NPs) have promising applications in high-density magnetic storage and magnetic nanocomposites. In this work, A novel method to yield SmCoparticles with small size and high coercivity was reported. Firstly, SmO-Co NPs with size of 6-15 nm were fabricated by a solvothermal route. Then the agglomerated SmCoparticles were obtained by thermal reduction of the precursor, which show high coercivity of2.0 T at room temperature. At last, the as-synthesized SmCoparticles were further hydrogenated under high hydrogen pressure of 4 MPa at room temperature, where hydrogen absorption process could form small-sized SmCoHparticles due to their lattice expansion and hydrogen desorption process could convert SmCoHNPs into SmCoNPs. The prepared SmCoNPs after hydrogenation, showing well distribution, have a small size of5-20 nm and room temperature coercivity of 1.22 T.
SmCo_5 nanoparticles(NPs) have promising applications in high-density magnetic storage and magnetic nanocomposites. In this work, A novel method to yield SmCo_5 particles with small size and high coercivity was reported. Firstly, Sm_2 O_3-Co NPs with size of 6-15 nm were fabricated by a solvothermal route. Then the agglomerated SmCo_5 particles were obtained by thermal reduction of the precursor, which show high coercivity of2.0 T at room temperature. At last, the as-synthesized SmCo_5 particles were further hydrogenated under high hydrogen pressure of 4 MPa at room temperature, where hydrogen absorption process could form small-sized SmCo_5 H_x particles due to their lattice expansion and hydrogen desorption process could convert SmCo_5 H_x NPs into SmCo_5 NPs. The prepared SmCo_5 NPs after hydrogenation, showing well distribution, have a small size of5-20 nm and room temperature coercivity of 1.22 T.
出处
《Rare Metals》
SCIE
EI
CAS
CSCD
2018年第12期1021-1026,共6页
稀有金属(英文版)
基金
financially supported by the National Natural Science Foundations of China (Nos. 51471016 and 51520105002)
the Key Natural Science Foundation of Beijing (No. 2151002)