摘要
高温变换炉在使用 2 2年后产生了很严重的氢腐蚀鼓包缺陷。对高温变换炉氢腐蚀的原因进行分析 ,采取去氢及增加内隔热层等办法 ,有效地延长了该设备的使用寿命。
After twenty two years of operation,the high temperature shift reactor has generated serious failure caused by hydrogen corrosion This paper analyses the reason of the hydrogen corrosion of the high temperature shift reactor Measures such as hydrogen diffusing and adding inner insulating layer were taken which have extended the service life of this equipment effectively
出处
《大氮肥》
CAS
2003年第4期228-230,共3页
Large Scale Nitrogenous Fertilizer Industry
关键词
高温变换炉
氢腐蚀
鼓包缺陷
内隔热层
去氢
合成氨
high temperature shift reactor,hydrogen corrosion,hydrogen diffusing,inner insulating layer