MnO 2 was prepared by column method from normal spinel LiMn 2O 4 with purity of 99.38%.The influence of LiMn 2O 4 grain size and acidity of leaching solution on the lithium leaching process was studied.The results show that the appropriate range of LiMn 2O 4 grain size was 60-160 meshes and the concentration of leaching solution HCl was 0.1 mol·L -1.The adsorption capacity Q of λ-MnO 2 for lithium increased with the increase of pH and changed markedly at pH 6.0-10.0.It was 3.80mmol/g at pH 12.0.The distribution coefficients K d of Li + and Na + were 3.406×10 4 and 2.300 respectively,and the separation coefficient α Li Na was 1.481×10 4 at pH 6.5.As a result,λ-MnO 2 is a high performance ion-sieve material for lithium ion.
MnO 2 was prepared by column method from normal spinel LiMn 2O 4 with purity of 99.38%.The influence of LiMn 2O 4 grain size and acidity of leaching solution on the lithium leaching process was studied.The results show that the appropriate range of LiMn 2O 4 grain size was 60-160 meshes and the concentration of leaching solution HCl was 0.1 mol·L -1.The adsorption capacity Q of λ-MnO 2 for lithium increased with the increase of pH and changed markedly at pH 6.0-10.0.It was 3.80mmol/g at pH 12.0.The distribution coefficients K d of Li + and Na + were 3.406×10 4 and 2.300 respectively,and the separation coefficient α Li Na was 1.481×10 4 at pH 6.5.As a result,λ-MnO 2 is a high performance ion-sieve material for lithium ion.
基金
theNationalNaturalScienceFoundationofChi na (No .5 9972 0 2 7)
theNaturalScienceFoundationofHubeiProvince (No .2 0 0 2AB0 74) )