The microstructure and creep behavior of a DS NiAI-Fe(Nb) multiphase intermetallic alloy have been investigated. This alloyexhibits dendritic structure, in which dendritic arm is β-(Ni,Fe)(Fe,Al) phase surrounded by interdendritic region of γ'/γ phase.The results of the creep test indicated that all of the creep curves have similar characteristic, which is a short primary creepstage and a dominant steady state creep stage, and the creep strain ranges from 18% to 52%. The apparent stress exponentand the apparent activation energy were analyzed and discussed. The mechanism of the creep deformation was also analyzedby the observation of TEM.
The microstructure and creep behavior of a DS NiAI-Fe(Nb) multiphase intermetallic alloy have been investigated. This alloyexhibits dendritic structure, in which dendritic arm is β-(Ni,Fe)(Fe,Al) phase surrounded by interdendritic region of γ'/γ phase.The results of the creep test indicated that all of the creep curves have similar characteristic, which is a short primary creepstage and a dominant steady state creep stage, and the creep strain ranges from 18% to 52%. The apparent stress exponentand the apparent activation energy were analyzed and discussed. The mechanism of the creep deformation was also analyzedby the observation of TEM.
基金
This work was supported by the National Natural Science Foundation of China (No.59895152)
National Advanced Materials Committee of China (No.863-715-005-0030), to whom we are very grateful.