A series of 0-3 composites of the polyvinylidene fluoride (PVDF) and BaTiO 3 was prepared.BaTiO 3 was modified with titanate coupling agent.The dielectric properties and the interfacial interaction of composites by different preparation methods were examined and compared.The result shows that the relative dielectric constant ε of the composite prepared in solution has a maximum value at about 70% weight fraction of BaTiO 3 and the dielectric loss tanδ increases rapidly when the fraction exceeds 70%.For the composite prepared in melt,the relative dielectric constant ε almost reaches a maximum value at about 60% weight fraction of BaTiO 3 and the dielectric loss is comparatively lower.The dielectric properties of composites are improved by using a coupling agent.
A series of 0-3 composites of the polyvinylidene fluoride (PVDF) and BaTiO 3 was prepared.BaTiO 3 was modified with titanate coupling agent.The dielectric properties and the interfacial interaction of composites by different preparation methods were examined and compared.The result shows that the relative dielectric constant ε of the composite prepared in solution has a maximum value at about 70% weight fraction of BaTiO 3 and the dielectric loss tanδ increases rapidly when the fraction exceeds 70%.For the composite prepared in melt,the relative dielectric constant ε almost reaches a maximum value at about 60% weight fraction of BaTiO 3 and the dielectric loss is comparatively lower.The dielectric properties of composites are improved by using a coupling agent.
基金
theNationalNaturalScienceFoundationofChina (No .5 0 172 0 10 )