A set of phosphate glasses with different amounts of Al2O3, Na2O, La2O3 and AlF3 contents were prepared to search for a phosphate glass which is suitable for ion-exchange process. Based on chemical durability test results and spectroscopic properties, a glass with excellent chemical durability and good spectroscopic properties is developed for ion-exchange process. The emission cross section of Er3+ in this glass is calculated to be 0.72×10~20 cm2 by McCumber theory. The planar waveguide with three modes at 632.8 nm and one mode at 1540 nm can be realized by 335℃ 3 hours ion-exchange in 5%AgNO3+95%KNO3 molten salt.
A set of phosphate glasses with different amounts of Al2O3, Na2O, La2O3 and AlF3 contents were prepared to search for a phosphate glass which is suitable for ion-exchange process. Based on chemical durability test results and spectroscopic properties, a glass with excellent chemical durability and good spectroscopic properties is developed for ion-exchange process. The emission cross section of Er3+ in this glass is calculated to be 0.72×10~20 cm2 by McCumber theory. The planar waveguide with three modes at 632.8 nm and one mode at 1540 nm can be realized by 335℃ 3 hours ion-exchange in 5%AgNO3+95%KNO3 molten salt.
基金
This work was supported by the Optical Science and Technology Program of Shanghai (No. 002261002)
B. Chen's e-mail address is chenbymail@yahoo.com.