摘要
A V4Ti alloy and several V4Cr4Ti alloys with different oxygen contents were studiedon their tensile properties with the effect of hydrogen concentrations.The ductility of the alloysshowed a successive decrease In a varied rate with an increased hydrogen concentration,while theultimate tensile strength remained unchanged or even decreased for the high oxygen content alloy
A V4Ti alloy and several V4Cr4Ti alloys with different oxygen contents were studied on their tensile properties with the effect of hydrogen concentrations. The ductility of the alloys showed a successive decrease in a varied rate with an increased hydrogen concentration, while the ultimate tensile strength remained unchanged or even decreased for the high oxygen content alloy in spite of the occurrence of hardening in the low oxygen content alloy. Oxygen in the alloy causes grain boundary weakening, increasing the possibility of intergranular fractures and thus enhancing the hydrogen embrittlement. V4Ti showed a higher resistance to the hydrogen embrittlement as compared to the V4Cr4Ti alloys on a similar oxygen content level.
基金
National Nature Science Foundation of China(No.50271025)