纳米蒙脱土对环氧树脂胶黏涂层性能的影响

Influence of NANO-MMT on the property of epoxy adhesive coating

研究了MMT-0、MMT、粉煤灰、B_4C作为填料在环氧树脂胶黏涂层中的作用。在WE/30液压万能试验机上测试其剪切强度,得出最佳配比是:MMT为5％,MMT-0为50％,粉煤灰为150％,B_4C为125％,在罐式浆体冲蚀磨损试验机上测试了最佳配比时涂层的冲蚀磨损率。结果表明:MMT作填料时剪切强度高,冲蚀磨损率低。

This paper studies the effect of MMT-0, MMT, fly ash, and B4C on epoxy adhesive. The shear strength are tested by on WE/30 universal hydraulic testing machine, the conclusion shows that the best packing's content is: 5% MMT, 50% MMT-0, 150% fly ash, 125% B4C. Then discusses their rate of solid particle erosion in pot liquid solid particle erosion testing machine. The experimental results show: The shear strength of epoxy res-in/MMT is high and the rate of solid particle erosion is low.