The effect of the mixed rare earths of Ce on the phase transformation in ascast ZA 27 alloy during compressive was investigated under 37 MPa and at 160 deg C by X-raydiffraction technique and SEM. The results showed that the as cast microstructure of ZA 27-RE alloyconsisted of a dendritic Al-rich alpha' surrounded by Zn-rich beta' phase, interdendritic epsilonphase and Zn-rich eta phase together with a complex Z phase which was a complex constitute compound,(RE,Cu)Al_5Zn_(16), dispersed in crystal interfaces or branch crystal interfaces and stable duringcompressive creep test at 160 deg C. The phase transformations of ZA 27-RE alloy, decomposition ofbeta' phase arid four transformation, were delayed by the addition of rare earths, also the lamellarstructure and the spheroidized structure in ZA 27-RE alloy were finer than in ZA 27 alloy duringcompressive creep test at 160 deg C at the same creep time, and the compressive creep resistance ofZA 27-RE alloy was higher than that of ZA 27 alloy.
The effect of the mixed rare earths of Ce on the phase transformation in ascast ZA 27 alloy during compressive was investigated under 37 MPa and at 160 deg C by X-raydiffraction technique and SEM. The results showed that the as cast microstructure of ZA 27-RE alloyconsisted of a dendritic Al-rich alpha' surrounded by Zn-rich beta' phase, interdendritic epsilonphase and Zn-rich eta phase together with a complex Z phase which was a complex constitute compound,(RE,Cu)Al_5Zn_(16), dispersed in crystal interfaces or branch crystal interfaces and stable duringcompressive creep test at 160 deg C. The phase transformations of ZA 27-RE alloy, decomposition ofbeta' phase arid four transformation, were delayed by the addition of rare earths, also the lamellarstructure and the spheroidized structure in ZA 27-RE alloy were finer than in ZA 27 alloy duringcompressive creep test at 160 deg C at the same creep time, and the compressive creep resistance ofZA 27-RE alloy was higher than that of ZA 27 alloy.