摘要
介绍了连铸钢几种常见的低倍组织缺陷,同时对其缺陷的定义、形貌特征进行了描述,并对缺陷产生的原因进行了分析。结合生产实际,说明了各种缺陷对产品加工的影响。对进厂原材料的质量检验提出了一些建议。
The paper introduced several common macrostructure defects of continuous casting steel,as well as the definition,characteristics and generation reason of these defects.The effects of different defects on product machining were presented based on production practice.Some suggestions on raw material quality inspection were given.
出处
《汽车工艺与材料》
2003年第12期15-18,共4页
Automobile Technology & Material
关键词
铸钢
组织
缺陷
加工
cast steel
structure
defect
machining