The influences of the flux KCl or KF on the XRD spectra, cell parameters and crystal appearance, and spectral properties of the phosphor LaMgB_5O_(10)∶Ce^(3+), Mn^(2+) were studied. The results indicate that when 4.2%, 8.6%, 12.8% KCl and 5.3%, 10.5%KF are respectively added into phosphor (La_(0.85)Ce_(0.15)) (Mg_(0.9)Mn_(0.1))B_5O_(10), compared with the normal card of JCPDS (No 35-120), the intensity of XRD spectra is enhanced, the values corresponded to 17/28, 18/28, 16/28, 18/28 and 2/28 and the cell parameters diminish because of the flux KCl and KF. The use of 5% KCl a fraction of Cu monocrystals are observed in the phosphor. There are six hexagonal crystal-faces and eight triangular crystal-faces representing crystal-face index {100} and {111}. When 15% KCl is added to the phosphor, law of crystal plane and self-regulaton are formed, the emission intensity of Ce^(3+) 5d-4f ((()~2F_(5/2),) (()~2F_(7/2))) and Mn^(2+) ((()~4G) and (()~6S)) increases by 3.41 times and 2.36 times respectively.
The influences of the flux KCl or KF on the XRD spectra, cell parameters and crystal appearance, and spectral properties of the phosphor LaMgB_5O_(10)∶Ce^(3+), Mn^(2+) were studied. The results indicate that when 4.2%, 8.6%, 12.8% KCl and 5.3%, 10.5%KF are respectively added into phosphor (La_(0.85)Ce_(0.15)) (Mg_(0.9)Mn_(0.1))B_5O_(10), compared with the normal card of JCPDS (No 35-120), the intensity of XRD spectra is enhanced, the values corresponded to 17/28, 18/28, 16/28, 18/28 and 2/28 and the cell parameters diminish because of the flux KCl and KF. The use of 5% KCl a fraction of Cu monocrystals are observed in the phosphor. There are six hexagonal crystal-faces and eight triangular crystal-faces representing crystal-face index {100} and {111}. When 15% KCl is added to the phosphor, law of crystal plane and self-regulaton are formed, the emission intensity of Ce^(3+) 5d-4f ((()~2F_(5/2),) (()~2F_(7/2))) and Mn^(2+) ((()~4G) and (()~6S)) increases by 3.41 times and 2.36 times respectively.
基金
NationalNaturalScienceFoundationofChina (2 0 2 610 0 6) ,NaturalScienceFoundationofJilinProviace(2 0 0 40 5 0 6 2 )