摘要
Polycrystalline samples La_(0.9-x)EuxSr_(0.1)MnO_3(x = 0.000, 0.075) were prepared by the standard solid-state reaction method. The results show that the samples preform a characteristic of clusters spin-glass state at low temperature. The samples show a characteristic of ferromagnetism(FM) characteristic in the temperature range of 15-125 K and 15-150 K respectively; the samples show preformed clusters in the temperature range of 125-343 K and 150-325 K, respectively, the samples show paramagnetism(PM)characteristic above 343 and 325 K, respectively. The second-order transitions are found at 118 and 135 K for undoped and doped sample, respectively. When the applied magnetic field is 7 T, the maximum magnetic entropy change |△S_M| value of the samples is near the Curie temperature(Tc), and the value of|△S_M| reaches 2.76 and 3.03 J/(K kg), respectively. In addition, the relative cooling power(RCP) is found to be 425.28 and 443.53 J/kg. The numerical fitting data fit well with experimental data. These results indicate that both the samples have the potential to realize magnetic refrigeration in the high temperature region(T > 77 K).
Polycrystalline samples La_(0.9-x)EuxSr_(0.1)MnO_3(x = 0.000, 0.075) were prepared by the standard solid-state reaction method. The results show that the samples preform a characteristic of clusters spin-glass state at low temperature. The samples show a characteristic of ferromagnetism(FM) characteristic in the temperature range of 15-125 K and 15-150 K respectively; the samples show preformed clusters in the temperature range of 125-343 K and 150-325 K, respectively, the samples show paramagnetism(PM)characteristic above 343 and 325 K, respectively. The second-order transitions are found at 118 and 135 K for undoped and doped sample, respectively. When the applied magnetic field is 7 T, the maximum magnetic entropy change |△S_M| value of the samples is near the Curie temperature(Tc), and the value of|△S_M| reaches 2.76 and 3.03 J/(K kg), respectively. In addition, the relative cooling power(RCP) is found to be 425.28 and 443.53 J/kg. The numerical fitting data fit well with experimental data. These results indicate that both the samples have the potential to realize magnetic refrigeration in the high temperature region(T > 77 K).
基金
Project supported by the State Key Development Program for Basic Research of China(11164019,51562032,61565013)
Inner Mongolia Natural Science Foundation(2015MS0109)
Research Program of Sciences at Universities of Inner Mongolia Autonomous Region of China(NJZZ11166,NJZY 16237,NJZY12202)
Young Science and Technology Foundation of Baotou Teachers'College(BSYKJ2014-22)