摘要
Effect of P-Na united modification on Al-22%Si-1.0%Cu-0.5%Mg-0.5%Mn alloy was studied. The results show that the refining effect of P-Na addition on primary silicon is superior to that of P and the former could modify eutectic silicon at the same time. Effects of P-Na modification on crystallization and microstructure of hypereutectic Al-Si alloys were studied with Electron-Scanning Microscope, Electron-Probe and X-ray diffractometer. The modification mechanism represents that on one hand, the primary silicon is refined by AlP as heterogeneous nucleus; on the other hand, when Na is added at the same time, P atoms are difficult to diffuse in the melt, and then enrichs on the growing faces of silicon phase. Moreover, a SiP compound was also discovered in Si crystals, which prevents the growth of silicon phase and refines the primary silicon.
Effect of P-Na united modification on Al-22%Si-1.0%Cu-0.5%Mg-0.5%Mn alloy was studied. The results show that the refining effect of P-Na addition on primary silicon is superior to that of P and the former could modify eutectic silicon at the same time. Effects of P-Na modification on crystallization and microstructure of hypereutectic Al-Si alloys were studied with Electron-Scanning Microscope, Electron-Probe and X-ray diffractometer. The modification mechanism represents that on one hand, the primary silicon is refined by AlP as heterogeneous nucleus; on the other hand, when Na is added at the same time, P atoms are difficult to diffuse in the melt, and then enrichs on the growing faces of silicon phase. Moreover, a SiP compound was also discovered in Si crystals, which prevents the growth of silicon phase and refines the primary silicon.
出处
《中国有色金属学会会刊：英文版》
CSCD
2003年第6期1285-1289,共5页
Transactions of Nonferrous Metals Society of China
关键词
过共晶AL-SI合金
铝合金
精练
添加剂
晶粒细化
hypereutectic Al-Si alloys
modification mechanism
grain refinement
modification