摘要
Cavitation erosion behavior of nickel-aluminum bronze(NAB) weldment in 3.5% NaCl aqueous solution was studied by magnetostrictive vibratory device for cavitation erosion. The results show that cavitation erosion resistance of the weld zone(WZ) of the weldment is superior to that of the base metal. SEM observation of eroded specimens reveals that the phases undergoing selective attack by the stress of cavitation erosion at the early stage of cavitation erosion are: martensite in the WZ, α phase in the heat-affected zone(HAZ) and eutectoidal phase in the base metal; the microcracks causing cavitation damage initiate at the phase boundaries.
Cavitation erosion behavior of nickel-aluminum bronze(NAB) weldment in 3.5% NaCl aqueous solution was studied by magnetostrictive vibratory device for cavitation erosion. The results show that cavitation erosion resistance of the weld zone(WZ) of the weldment is superior to that of the base metal. SEM observation of eroded specimens reveals that the phases undergoing selective attack by the stress of cavitation erosion at the early stage of cavitation erosion are: martensite in the WZ, α phase in the heat-affected zone(HAZ) and eutectoidal phase in the base metal; the microcracks causing cavitation damage initiate at the phase boundaries.
出处
《中国有色金属学会会刊：英文版》
CSCD
2003年第6期1317-1324,共8页
Transactions of Nonferrous Metals Society of China
基金
Project((11H1004)supportedbytheNationalDefenceFoundationofChina