The dynamic strain aging behavior during tensile tests of K40S alloy has been investigated in the temperature range of 25-1100℃ with the strain rate range from 10-4 to 10-3s-1. The results show that four different types of serration, identified as A, B, C and E type serration were observed in the temperature range of 300-600℃. The strain exponents for onset of the serrated flow were calculated as 1.21, 2.19 and 1.61, and the activation energies as 121, 40 and 67kJ/mol for E, B and C type serration respectively. The main mechanism for dynamic strain aging discussed in light of the strain exponent and the activation energy.
The dynamic strain aging behavior during tensile tests of K40S alloy has been investigated in the temperature range of 25-1100℃ with the strain rate range from 10-4 to 10-3s-1. The results show that four different types of serration, identified as A, B, C and E type serration were observed in the temperature range of 300-600℃. The strain exponents for onset of the serrated flow were calculated as 1.21, 2.19 and 1.61, and the activation energies as 121, 40 and 67kJ/mol for E, B and C type serration respectively. The main mechanism for dynamic strain aging discussed in light of the strain exponent and the activation energy.