纳米SiO_X改性不饱和聚酯树脂 被引量:10

UP Resin Modified with Nano SiO_X
下载PDF
导出
摘要 用纳米SiOX 粒子对 2 98# 不饱和聚脂 (UPR)进行增强、增韧改性 ,发现随粒子用量增加 ,树脂凝胶时间、粘度增大 ;粒子用量为 0 .5 %时树脂有脆韧转变现象 ;用量为 3%时 ,拉伸强度和断裂延伸率分别提高约 33%和 6 0 %。用KH - 5 70偶联剂进行表面处理有助于提高纳米SiOX 粒子在UPR中的均匀分散。 The type 298# UPR(Unsaturated Polyester Resin)was toughened and strengthened by using the nanometer SiO X powder. The results show that gel time and viscosity of 298# UPR increased greatly while increasing the content of nanometer SiO X powder; an brittle-tough transformation was observed at the critical content of 0.5% of nanometer SiO X powder. The tensile strength and elongation at break of the resin increase by 33% and 60% from the pure resin respectively when the content of nanometer SiO X is 3%. SiO X powder surface treatment with the KH-570 coupling agent can improve uniform dispersing of nanometer SiO X in the resin.
出处 《纤维复合材料》 CAS 2003年第4期14-17,共4页 Fiber Composites
关键词 纳米SIOX 改性 不饱和聚酯树脂 增强 增韧 脆韧转变 nanometer SiO X,modify,UPR,toughen,strengthen,brittle-tough transformation
  • 相关文献

参考文献1

二级参考文献1

  • 1Wang Guozhong Wang Zhongchang.-[J].材料研究学报,1997,11(5):527-527.

共引文献12

同被引文献194

引证文献10

二级引证文献32

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部