The preparation of ZnAlLa-hydrotalcite-like compounds [ZnAlLa-HTLcs] wasstudied. ZnAlLa-HTLcs were synthesized by a method of variable pH with the raw materials ofZn(NO_3)_2, Al(NO_3)_3, La(NO_3)_3, and NaOH. The eS'ccts of some factors (i.e. pH values, the moleratio of Al^(3+) to La^(3+), temperature and the period of hydrothermal treatment) on thepreparation of HTLcs were discussed systematically. XRD, TG-DTA, FT-IR spectroscopy, and ICP wereperformed to characterize ZnAlLa-HTLcs samples, and the thermal stability of HTLcs was alsodiscussed. It was shown that unique ZnAlLa-HTLcs with high crystallinity can be prepared, under theconditions of pH = 5.5-6.5, n(Zn^(2+))/n(Al^(3+) + La^(3+))=2 and the atomic ratio of La^(3+) toAl^(3+) ranging from 0.07 to 2, hydrothermal treatment at 120 ℃ for 5 h. When the calcination ofthe HTLcs is performed at temperatures above 200 ℃, ZnO phase is detected with Al_2O_3 and La_2O_3spreading on its top. The complex metal oxides derived from ZnAlLa-HTLcs at 500 ℃ have highercatalytic activity and selectivity than those from ZnAl-HTLcs for the esterification of acetic acidwith n-butanol under the same reaction conditions.
The preparation of ZnAlLa-hydrotalcite-like compounds [ZnAlLa-HTLcs] wasstudied. ZnAlLa-HTLcs were synthesized by a method of variable pH with the raw materials ofZn(NO_3)_2, Al(NO_3)_3, La(NO_3)_3, and NaOH. The eS'ccts of some factors (i.e. pH values, the moleratio of Al^(3+) to La^(3+), temperature and the period of hydrothermal treatment) on thepreparation of HTLcs were discussed systematically. XRD, TG-DTA, FT-IR spectroscopy, and ICP wereperformed to characterize ZnAlLa-HTLcs samples, and the thermal stability of HTLcs was alsodiscussed. It was shown that unique ZnAlLa-HTLcs with high crystallinity can be prepared, under theconditions of pH = 5.5-6.5, n(Zn^(2+))/n(Al^(3+) + La^(3+))=2 and the atomic ratio of La^(3+) toAl^(3+) ranging from 0.07 to 2, hydrothermal treatment at 120 ℃ for 5 h. When the calcination ofthe HTLcs is performed at temperatures above 200 ℃, ZnO phase is detected with Al_2O_3 and La_2O_3spreading on its top. The complex metal oxides derived from ZnAlLa-HTLcs at 500 ℃ have highercatalytic activity and selectivity than those from ZnAl-HTLcs for the esterification of acetic acidwith n-butanol under the same reaction conditions.
基金
Supported by Shanxi Province Natural Science Funds.(20001015)