SrCe_(0.95)Yb_(0.05)O_(3-α)的直接固相法制备及其导电性能 被引量:3

Preparation of direct solid-state reaction and conductivity of SrCe_(0.95)Yb_(0.05)O_(3-α) protonic conduction
下载PDF
导出
摘要 采用改进的直接固相合成工艺,制备了SrCe0.95Yb0.05O3-α固体电解质。应用AUTOLABPGSTAT30型电化学工作站测定了不同温度和不同气氛下SrCe0.95Yb0.05O3-α的阻抗谱,在350~800℃内电导率为6.3×10-5~4.8×10-3S/cm,计算得到电导活化能分别为0.63eV(空气气氛下),0.46eV(水蒸气气氛下)。研究结果表明,该工艺方法简单,能避免材料制备过程中杂质的混入,且制得的SrCe0.95Yb0.05O3-α高温质子导体电性能良好。 SrCe_(0.95)Yb_(0.05)O_(3-α) was prepared by direct solid-state reaction. The AC impedance spectrums of SrCe_(0.95)-(Yb_(0.05))O_(3-α) were measured by AUTOLAB PGSTAT30 electrochemical measuring device at different testing temperatures and gas atmospheres. The conductivity of the electrolyte was 6.3×10^(-5)~4.8×10^(-3) S/cm at the temperature range of 350~800℃. The activation energies were 0.63eV and 0. 46eV in air and water vapor, respectively. The results show that the improved technique is convenient. It can keep impurity out of the preparing procedure. The prepared high temperature protonic conduction SrCe_(0.95)Yb_(0.05)O_(3-α) has good electric performance.
出处 《中国有色金属学报》 EI CAS CSCD 北大核心 2004年第1期42-46,共5页 The Chinese Journal of Nonferrous Metals
基金 上海市教委重点基金资助项目(01AZ01)
关键词 固相合成法 高温质子导体 阻抗谱 活化能 导电性能 固体电解质 solid-state reaction high temperature protonic conduction AC impedance spectrums activation energies
  • 相关文献

参考文献14

  • 1[1]Talbot D E J, Anyalebechi P N. Solubility of hydrogen in liquid aluminum[J]. Materials Science and Technology, 1988, 4(1): 1-4.
  • 2[2]Ichimura M, Sasajima Y. Effect of purity on diffusivity and solubility of hydrogen in aluminum[J]. Materials Transactions, JIM, 1992, 33(5): 449-453.
  • 3[3]Birnbaum H K, Buckley C. Hydrogen in aluminum[J]. Journal of Alloys and Compounds, 1997, 253-254: 260-264.
  • 4[4]Lin R Y, Hoch M. The solubility of hydrogen in molten aluminum alloys[J]. Metall Mater Trans A, 1989, 20A: 1785-1791.
  • 5[5]Anyalebechi P N. Analysis of the effects of alloying elements on hydrogen solubility in liquid aluminum alloys[J]. Scripta Metallurgica et Materialia, 1995, 33(8): 1209-1216.
  • 6[6]Anyalebechi P N. Attempt to predict to hydrogen solubility limits in liquid multi-component aluminum alloys[J]. Scripta Materialia, 1996, 34(4): 513-517.
  • 7[8]Iwahara H, Esaka T, Uchida H, et al. Proton conduction in sintered oxides and its application to steam electrolysis for hydrogen production[J]. Solid State Ionics, 1981, (3-4): 358-363.
  • 8[9]Uchida H, Maeda N, Iwahara H. Relation between proton and hole conduction in SrCeO3-based solid electrolytes under water-containing atmospheres at high temperatures[J]. Solid State Ionics, 1983, 11(2): 117-124.
  • 9[10]Yajima T, Iwahara H, Uchida H, et al. Relation between proton conduction and concentration of oxide ion vacancy in SrCeO3 based sintered oxides[J]. Solid State Ionics, 1990, 40-41: 914-917.
  • 10[11]Shin S, Huang H, Ishigame M, et al. Protonic conduction in the single crystals of SrZrO3 and SrCeO3 doped with Y2O3[J]. Solid State Ionics, 1990, 40-41: 910-913.

同被引文献28

引证文献3

二级引证文献3

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部