氢对Ti-4Al-2V疲劳裂纹扩展速率的影响 被引量:7

Effects of hydrogen on fatigue crack propagation rate of Ti-4Al-2V alloy
下载PDF
导出
摘要 采用CT试样对4种含氢量不同的Ti 4Al 2V钛合金的室温疲劳裂纹扩展速率进行了实验测定,并对断裂以后的试样进行了断口观察。实验结果表明:含氢的Ti 4Al 2V材料的稳态裂纹扩展行为符合Paris幂律关系,氢对裂纹稳态扩展区和失稳扩展区的da/dN基本没有影响,但对近门槛扩展行为有明显影响;与自然含氢量的材料相比,高含氢量的材料疲劳裂纹在近门槛扩展区的速率明显较低。 The CT specimens of Ti4Al2V alloy bearing four different hydrogen contents were employed to measure the fatigue crack propagation rate at room temperature and the fracture surfaces were observed. The results reveal that the behavior of stable crack propagation is in a good accordance with the Paris Law, and the hydrogen has little effect on da/dN in stable crack propagation stage and rapid rupture stage, but has remarkable effect on da/dN in nearthreshold crack growth. Compared with the material of natural hydrogen content, the materials with higher hydrogen concentration show lower crack growth rate within nearthreshold stage.
作者 何晓 沈保罗
出处 《中国有色金属学报》 EI CAS CSCD 北大核心 2003年第4期924-927,共4页 The Chinese Journal of Nonferrous Metals
关键词 钛合金 疲劳 断口 裂纹扩展速率 hydrogen titanium alloy fatigue fracture morphology
  • 相关文献

参考文献1

  • 1褚武扬.氢损伤和滞后断裂[M].北京:冶金工业出版社,1988..

共引文献41

同被引文献84

引证文献7

二级引证文献25

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部